a1_Mechanical properties of scaffolds seeded with mesenchymal stem cells used for cartilage repair seem to be one of the critical factors in possible joint resurfacing. In this paper, the effect of adding hyaluronic acid, hydroxyapatite nanoparticles or chitosan nanofibers into the cross-linked collagen I on the mechanical response of the lyophilized porous scaffold has been investigated in the dry state at 37 oC under tensile loading. Statistical significance of the results was evaluated using ANOVA analysis. The results showed that the addition of hyaluronic acid significantly (p<<0.05) reduced the tensile elastic modulus and enhanced the strength and deformation to failure of the modified cross-linked collagen I under the used test conditions. On the other hand, addition of hydroxyapatite nanoparticles and chitosan nanofibers, respectively, increased the elastic modulus of the modified collagen ten-fold and four-fold, respectively. Hydroxyapatite caused significant reduction in the ultimate deformation at break while chitosan nanofibers enhanced the ultimate deformation under tensile loading substantially (p<<0.05). The ultimate tensile deformation was significantly (p<<0.05) increased by addition of the chitosan nanofibers. The enhanced elastic modulus of the scaffold was translated into enhanced resistance of the porous scaffolds against mechanical load compared to scaffolds based on cross-linked neat collagen or collagen with hyaluronic acid with similar porosity. It can be concluded that enhancing the rigidity of the compact scaffold material by adding rigid chitosan nanofibers can improve the resistance of the porous scaffolds against compressive loading, which can provide more structural protection to the seeded mesenchymal stem cells when the construct is implanted into a lesion., a2_Moreover, scaffolds with chitosan nanofibers seemed to enhance cell growth compared to the neat collagen I when tested in vitro as well as the scaffold stability, extending its resorption to more than 10 weeks., J. Jančář, A. Slovíková, E. Amler, P. Krupa, H. Kecová, L. Plánka, P. Gál, A. Nečas., and Obsahuje bibliografii
Understanding the behavior of single proteins at the polyelectrolyte multilayer film/solution interface is of prime importance for the designing of bio-functionalized surface coatings. In the present paper, we study the adsorption of the model proteins, albumin and lysozyme, as well as basic fibroblast growth factor (FGF-2) on a polysaccharide multilayer film composed of quaternized chitosan and heparin. Several analytical methods were used to describe the formation of the polysaccharide film and its interactions with the proteins. Both albumin and lysozyme adsorbed on quaternized chitosan/heparin films, however this process strongly depended on the terminating polysaccharide. Protein adsorption was driven mainly by electrostatic interactions between protein and the terminal layer of the film. The effective binding of FGF-2 by the heparinterminated film suggested that other interactions could also contribute to the adsorption process. We believe that this FGF-2- presenting polysaccharide film may serve as a biofunctional surface coating for biologically-related applications., M. Kumorek, D. Kubies, T. Riedel., and Obsahuje bibliografii
A combined sorbent was prepared by impregnation of lignite mined in the South Moravian Coalfield, Czech Republic, with chitosan. Sorption performance of the combined sorbent and the untreated lignite was tested for Co(II), Cu(II), and Cd(II) in equilibrium sorption experiments with respect to pH and metal concentration. The amount of metal retained by the sorbent was determined by instrumental neutron activation analysis in the short time irradiation mode with epithermal neutrons. For pH~5, sorption isotherms were determined and fitted using the Langmuir and Freundlich models. The results have been compared with those obtained previously for similar combined sorbent based on naturally oxidized coal mined in the Sokolov Basin, Czech Republic. It has been shown that the effect of chitosan on sorption efficiency of the chitosan-doped coal sorbents strongly depends on solution pH, and type of coal and metal., Martina Havelcová, Jiří Mizera, Vladimír Machovič, Lenka Borecká, Oldřich Přibyl and Ivana Krausová., and Obsahuje bibliografii