Disc-shaped metal elements, composed of different types of steel - stainless 1.4305 and 1.4301, tool steel toolox 44 - were polished to a high quality. Polishing was performed by means of classical approach of autorotational horizontal-swinging kinematics, using polishing cloth and diamond polishing slurries. Elements of all tested types of steel exhibited surface damage described as pitting. This form of defects was least significant for elements made of the harder tool steel, which exhibited overall best quality of polished surface. Furthermore, experiments with polishing of NiP layers deposited on already polished elements’ surface were described. and Kovové elementy ve tvaru disků, zhotovené z nerezových ocelí 1.4305 a 1.4301 a nástrojové oceli toolox 44, byly leštěny na vysokou kvalitu. Leštění bylo provedeno klasickými postupy autorotační kývavé kinematiky s použitím textilní podložky a diamantových lešticích disperzí. U elementů všech typů ocelí byl pozorován výskyt povrchových defektů v podobě tzv. pittingu. Nejméně výrazná byla tato forma defektů u elementů z tvrdší nástrojové oceli, které vykazovaly celkově nejlepší kvalitu leštěných povrchů. Dále jsou popsány experimenty leštění vrstev NiP nanesených na již vyleštěných ocelových elementech.