In presented work, raw, expanded and acid treated vermiculites were used as low-cost and active adsorbents for reducing of environmental pollution with heavy metals. Acid treatment was performed at elevated temperature (95°C) for 2 and 24 h in solution of HNO3. Adsorption capacity towards Fe3+ was studied in column, semi-batch and batch mode. It was shown that all samples are effective in removal of heavy metals; however adsorption mechanism is based not only on ion exchange of interlayer cations but also precipitation/deposition processes. Starting material and modified samples as well as spent adsorbents were characterized with respect to the vermiculite structure using X-ray diffraction method., Agnieszka Węgrzyn, Lucjan Chmielarz, Paweł Zjeżdżalka, Andrzej Kowalczyk, Magdalena Jabłońska, Xavier Baldrich Tolosa and Marek Michalik., and Obsahuje bibliografii
Adsorption of phenol and aniline onto original and with quaternary ammonium salts (QASs)-modified montmorillonite was described by sorption isotherms of type III and II, respectively. For the montmorillonite (MMT) modification - hydrophobisation, cetyltrimethyl- ammonium (CTMA) and tetramethylammonium (TMA ) cations were used. In comparison with phenol, aniline was adsorbed largely on original MMT but less on modified one. XRD pa tterns indicated that both aromatic compounds were intercalated in the MMT interlayer be ing perpendicularly oriented to silicate sheets. Alkyl chains of CTMA and TMA probably act as organic "pillars" stabilising the MMT tabular structure against exfoliation due to the intercalation with phenol and aniline of high concentrations., Hana Kostelníková, Petr Praus and Martina Turicová., and Obsahuje bibliografické odkazy
Phenolic compounds are common pollutants found particularly in the effluents from petroleum and petrochemical, coal conversion, and phenol producing industries. Due to their toxicity and carcinogenity, water and wastewater containing phenolic compounds must be treated before being used and discharged for receiving water bodies. There is a growing interest in using low-cost and commercially available materials for the adsorption of organic compounds. Clay minerals have great potential to remove phenols in water due to efficient sorbents which can be used as alternative adsorbents to replace the costly activated carbon. They are widely applied in many fields of adsorption technology including the removal of amines, metals, ketones, phosphates, chlorophyll, non-ionic contaminants, and organic pigments/dyes. Montmorillonitic smectites, {(Na,Ca)0.33(Al,Mg)2(Si4O10)-(OH)2.nH2O} are one of the natural clay minerals that have specific surface chemical properties. In this study, a factorial experimental design technique was used to investigate the adsorption of phenol from water solution on montmorillonite. Factorial design of experiments is employed to study the effect of three factors: pH (2.0 and 8.0), montmorillonite dosage (0.1 and 1.0 g/L) and initial low and high concentration (10 and 100 mg/L). The efficiency of phenol adsorption was determined after 60 min of treatment. Main effects and interaction effects of three factors were analyzed by using statistical techniques. A regression model was found to fit the experimental data very well. Through using the Student’s t-test, analysis of variance, F-test and lack of fit to define most important process variables affecting the percentage phenol adsorption., Feza Geyikçi and Semra Çoruh., and Obsahuje bibliografii
Purification of quartz using an environment-friendly method is important in the contaminants removal. This paper presents advanced method based on calcination pretreatment combined with ultrasound-assisted leaching, for removing iron impurities from industrial quartz. The solvent used is a mixture comprised by diluted hydrochloric acid and oxalic acid. The effects of experimental parameters were investigated and the purification mechanism was discussed using particle size analyzer, scanning electron microscope and polarized light microscope. SiO2 content of concentrate could be increased from 99.6828% to 99.9047%, which achieved 3N level high purity quartz, and Fe2O3 content reduced from 0.0857% to 0.0223%, under the optimal conditions, i.e., calcination temperature of 900 °C, holding time of 2 h, oxalic acid concentration of 10 g/L, hydrochloric acid concentration of 5%, liquid solid ratio of 5, leaching temperature of 60 °C, ultrasound power of 400 W and treatment time of 30 min. Compared to conventional method, the proposed method significantly accelerates the leaching process and increases the iron removal rate. At the same time, the method also can remove gas-liquid inclusions. and Yang Changqiao, Li Suqin, Bai Jiaxing, Han Shuaishuai.
Aerial photogrammetry was chosen as an additional observation method of the subsidence depression that was created above exploited coal mining panels near Karviná. While individual points of a permanent observation network were repeatedly surveyed by GNSS, the whole subsidence depression was surveyed by the aerial photogrammetry. As this method was applied three times (during three years) we can compare its results in individual years and observe the major surface changes on the undermined area. Also, a comparison was realized between the points’ coordinates gained from both aerial photogrammetry and GNSS. The results show that the method of aerial photogrammetry enriches and complements the GNSS observation in monitoring the spatial development and shape of the subsidence depression, especially in the areas of active recultivation., Vlastimil Kajzar, Hana Doležalová, Kamil Souček and Lubomír Staš., and Obsahuje bibliografii
Irreversible moisture expansion of specimens made from porous ceramics of historical fired tiles is analysed here. Irreversible moisture expansion values, which reflect the rate of body ageing, were determined by heating at a temperature of 650 °C for 20 minutes and by repeated dilatometric measurement until a te mperature of 700 °C. To evaluate body ageing due to moisture expansion, it is necessary to specify the non-crystalline phase content. The causative factors influencing body ageing can be determined on bodies that have comparable non-crystalline phase content and are of similar chemical and mineralogical composition. Sufficient data set may facilitate a roughestimate of the age of historical ceramics., Vladimír Hanykýř, Alexandra Koužková, Petr Bouška and Miroslav Vokáč., and Obsahuje bibliografické odkazy